PTFE SKIVED SHEET, TAPE & FILM
Features
PTFE resin is first molded into work-blank and then skived. The PTFE resin skived sheet & tape are highly dielectric. Chemical resistant and not aging. They have a wide range of operation temperature.
1. PTFE Skived Sheet Tape
Main properties
Property | Unit | Result |
Appetent density | g/cm3 | 2.10-2.30 |
Tensile strength (min) | MPa | ≥15.0 |
Ultimate elongation (min) | % | 150% |
Dialectic strength | KV/mm | 10 |
Specifications
Property | Code name |
Skived sheet | Thickness 0.5-3 |
Width 900.1000.1200 | |
Length≥200 | |
Skived tape | Thickness 0.5-4 |
Width 100-500 | |
Length≥1000 |
2. PTFE Skived Film
Main properties
Item | Thickness |
Thickness allowance |
Thickness |
Widt hallowance |
Length |
high-density | 0.015,0.030 | ±10% | 30-90 | ±0.3 | ≥50 |
0.020,0.035 | |||||
0.025,0.040 | |||||
semi-density | 0.030,0.035 | ±10% | 60-90 | ±0.3 | ≥100 |
0.05-0.10 | |||||
common | 0.020,0.025 | ±10% | 60-90 | ±2.0 | ≥50 |
0.030,0.035 | |||||
0.040-0.10 |
Specifications
Property | Unit | High-density | Semi-density | Common |
Tensile strength | MPa | ≥30 | ≥20 | ≥10 |
Elongation at rupture | % | ≥30 | ≥60 | ≥100 |
1MHz dielectric loss tangent | 2.5×10-4 | -- | -- | |
1MHz dielectric constant | average 1.8-2.2 | - | -- | |
Dc breakdown voltage (Normal temperature) |
KV/M | average 200 | average 60 | average 30 |
lowest 40 | lowest 6 |
Applications
Lining,seaing and oil less lubricating material and dielectric at any frequencies. Capacitor dielectric, wire isolation, electrical instrument isolation.
1. What is your MOQ?
MOQ may vary by customer's special requirement; we try our best to meet your business requirement.
2. What's your payment terms?
We normally do T/T, and we can also offer western union account for transfer money. And more flexible payment terms, welcome to have a discuss.
3. Can you provide samples?
Yes, we can offer samples, and some samples are free
4. Can you delivery by express?
Yes, we can delivery by any express.
5. When will the sample be ready?
Normally, the sample can be ready in 3 days.